TY - GEN
T1 - Mechanical profiling of commercial grade biodegradable plastic films post exposure to natural and accelerated weathering
AU - Al-Salem, Sultan Majed
AU - Al-Nasser, Afaf Ya’Qoub
AU - Al-Wadi, Majed Hameed
AU - Sultan, Hanan Hmoud
AU - Karam, Hajar Jawad
AU - Al-Dhafeeri, Ayyad Toman
AU - Al-Foudaree, Mohammad
AU - Rasheed, Zakia
N1 - Publisher Copyright:
© 2019 WIT Press.
PY - 2019
Y1 - 2019
N2 - Market standards for plastic products are typically governed by mechanical properties that manufacturers and converters adhere to. However, in the case of biodegradable plastic film products, namely bags used on the market, the standards must convey more environmentally related factors. In this paper, mechanical profiling of three commercial grade market products were tested. The plastic films were deemed biodegradable of oxo-biodegradable nature containing calcium carbonate (CaCO3) amongst other prodegradant chemical agents. The evaluation of mechanical properties was conducted in laboratory conditions to determine the impact of exposing the samples to various degradation media, in accordance to ASTM D 882. Experiments were conducted using a universal testing machine (50 kN load cell) set to a 500 mm min-1 test speed. The measured properties included Young’s modulus (MPa), ultimate stress (MPa), ultimate strain (%), stress at break (MPa), strain at break (%) and force at break (N). The width and thickness of the film specimens were measured using an internally calibrated Vernier callipers to the nearest 0.1 mm. Processing and cutting variation was minimal between the width and the thickness over the length of some samples accounting for less than 1% of total number of samples measured. The determination of the mechanical properties was conducted post accelerated and natural weathering as per the standard test methods of ASTM D 4329 and ASTM D 5272, respectively. Statistical analysis utilizing the means of one-way analysis of variance (ANOVA) was also conducted among the samples exposed to natural weathering with respect to variables of meteorological conditions and primary/secondary airborne pollutants. The change of the mechanical properties has led to the understanding of the response of polymeric films deemed as biodegradable in response to exposure to natural environment, where waste minimization and standard development can be achieved for future mitigation.
AB - Market standards for plastic products are typically governed by mechanical properties that manufacturers and converters adhere to. However, in the case of biodegradable plastic film products, namely bags used on the market, the standards must convey more environmentally related factors. In this paper, mechanical profiling of three commercial grade market products were tested. The plastic films were deemed biodegradable of oxo-biodegradable nature containing calcium carbonate (CaCO3) amongst other prodegradant chemical agents. The evaluation of mechanical properties was conducted in laboratory conditions to determine the impact of exposing the samples to various degradation media, in accordance to ASTM D 882. Experiments were conducted using a universal testing machine (50 kN load cell) set to a 500 mm min-1 test speed. The measured properties included Young’s modulus (MPa), ultimate stress (MPa), ultimate strain (%), stress at break (MPa), strain at break (%) and force at break (N). The width and thickness of the film specimens were measured using an internally calibrated Vernier callipers to the nearest 0.1 mm. Processing and cutting variation was minimal between the width and the thickness over the length of some samples accounting for less than 1% of total number of samples measured. The determination of the mechanical properties was conducted post accelerated and natural weathering as per the standard test methods of ASTM D 4329 and ASTM D 5272, respectively. Statistical analysis utilizing the means of one-way analysis of variance (ANOVA) was also conducted among the samples exposed to natural weathering with respect to variables of meteorological conditions and primary/secondary airborne pollutants. The change of the mechanical properties has led to the understanding of the response of polymeric films deemed as biodegradable in response to exposure to natural environment, where waste minimization and standard development can be achieved for future mitigation.
KW - Biodegradable plastic
KW - Oxo-biodegradable
KW - Polymer
KW - Strain
KW - Stress
UR - http://www.scopus.com/inward/record.url?scp=85075661848&partnerID=8YFLogxK
U2 - 10.2495/MC190221
DO - 10.2495/MC190221
M3 - Conference contribution
AN - SCOPUS:85075661848
SN - 9781784663315
T3 - WIT Transactions on Engineering Sciences
SP - 229
EP - 242
BT - Materials and Contact Characterisation IX
A2 - Hernández, S.
A2 - De Hosson, J.
A2 - Northwood, D.O.
A2 - Vilar, R.
PB - WITPress
T2 - 9th International Conference on Computational Methods and Experiments in Material and Contact Characterisation, 2019
Y2 - 22 May 2019 through 24 May 2019
ER -